Mark

C

Cr

Mo

W

V

Co

P

S

Mn

Si

Fe

Hardness   HRC

T15

1.50¡«1.60

3.75¡«5.00

≤1.00

11.75¡«13.00

4.50¡«5.25

4.75¡«5.25

≤0.02

≤0.02

≤0.05

≤0.05

Bal.

66¡«69

M3

1.25¡«1.35

3.90¡«4.50

4.70¡«5.50

5.90¡«6.70

2.75¡«3.25

-

≤0.02

≤0.02

≤0.05

≤0.05

Bal.

65¡«67

M2

0.80¡«0.90

3.80¡«4.40

4.50¡«5.50

5.50¡«6.75

1.75¡«2.20

-

≤0.02

≤0.02

≤0.05

≤0.05

Bal.

65¡«67

10V

2.4¡«2.5

5¡«5.5

≤1.3

-

9.5¡«10.5

-

≤0.02

≤0.02

≤0.05

≤0.05

Bal.

67¡«70

Mark

Co

Cr

Mo

W

Al

Ti

Nb

C

Zr

B

Ta

Ni

Rene95

8±1

13±1

3.5±0.2

3.5±0.2

3.5±0.2

3.5±0.2

8±0.2

0.07±0.02

0.05±0.02

0.01±0.05

--

Bal.

Rene104

20.6±1

13±1

3.8±0.3

2.1±0.2

3.4±0.2

3.7±0.2

20.6±0.2

0.05±0.02

0.05±0.02

0.025±0.05

2.4±0.2

Bal.

718

≤1

17-21

3.8-3.3

--

0.2-0.8

0.65-1.15

4.75-5.5

≤0.08

--

≤0.006

Bal.

50-55

625

--

20-23

8¡«10

--

≤0.25

≤0.25

3.15-4.15

≤0.1

--

--

--

Bal.

FGH-12

Bal.

30.0-32

≤1.0

9-9.5

--

--

--

1.5-1.7

--

--

--

0.4-1.5(Si)

Ti6Al4V

--

--

--

--

5.5-6.75

Bal.

--

≤0.1

--

--

--

3.5-4.5(V)