Type |
Product Name |
Size |
Specification and Application |
KF-310 |
Fe15Cr1B1Si
Iron-base alloy powder |
-140+325目（mesh） |
HRC 25, (Working Temperature): ≤600℃.
Moderate hardness, excellent toughness. Hard to crack when spraying thick coating. Used to repair work-pieces size and increase wear resistant life in Oxyacetylene Flame Spraying, such as paper-making dryer and shaft. |
KF-311 |
Fe15Cr1B1Si10Ni
Iron-base alloy powder |
-140+325目（mesh） |
HRC 25, (Working Temperature): ≤600℃.
Excellent toughness. Hard to crack when spraying thick coating. Restoring parts and wearing treatment in Oxyacetylene Flame Spraying. Optimum for restoring shaft. |
KF-316L |
Fe17Cr12M1Si2.4Mo0.1Mn
Iron-base alloy powder |
-140+325目（mesh）
-45+15µm |
HRC 25, (Working Temperature): ≤540℃.
Excellent toughness. Used in Laser Cladding. Plasma Welding, Flame Spraying and Plasma Spraying. Used as the repairing of turbine blade, injecting nozzle, ring, diesel cylinder etc. |
KF-JG-2 |
Fe17Cr20Ni4Mo1Mn
Iron-base alloy powder |
-140+325目（mesh） |
HRC 28-32, (Working Temperature): ≤540℃.
Used in Laser cladding, Plasma welding, Plasma spraying and HVOF. Used for working layer of wear resistant and corrosion resistant parts such as Hydraulic rod. |
KF-Fe901 |
Fe13Cr1.6B1.2Si0.8Mo
Iron-base alloy powder |
-140+325目（mesh） |
HRC 55, (Working Temperature): ≤540℃.
High toughness. Excellent crack resistance. Applied for laser cladding and plasma surfacing. Laser cladding, Plasma welding for corrosion resistant working welding layering of shaft. |
KF-Fe62 |
Fe5C1Si1.8B43Cr
Iron-base alloy powder |
-140+325目（mesh） |
HRC 62-67, (Working Temperature): ≤540℃.
High coating hardness, excellent wear resistance. Used as deposited corrosion resistant of petroleum rods, water turbine blade, blast furnace top bell, mud pump, breaking machine, backing block etc. |
KF-Fe33-37 |
Fe21Cr1.5B3.5Si10Ni2Mo0.8Mn0.5V |
-140+325目（mesh） |
HRC 33-37, (Working Temperature): ≤540℃.
Moderate hardness. Excellent crack resistance and bead smooth. Used for valve, thermal resistance idler roller in plasma welding. |
DF-Fe37-43 |
Fe21Cr1.7B3.5Si10Ni2Mo0.8Mn0.7V
Iron-base alloy powder |
-140+325目（mesh） |
HRC 37-463, (Working Temperature): ≤450℃.
Better used mating with Fe33-37. Used for valve sealing in plasma surfacing. |
KF-D507 |
Fe87Cr13
Iron-base alloy powder |
-140+325目（mesh） |
HRC 30-35, (Working Temperature): ≤450℃.
Used for carbon steel or alloy steelworkpiece surfacing welding when operating temperature below 450℃. For example, plasma welding shaft and moderate temperature high pressure valve, which is air quenching. |
KF-D507Mo |
Fe6Ni2W13Cr2.5Mo2.5
Iron-base alloy powder |
-140+325目（mesh） |
HRC 35-40, (Working Temperature): ≤450℃.
Deposited metals with high temperature hardness, good thermal stability, erosion resistance. Plasma welding, medium temperature and high pressure valve welding, which is characteristic of air quenching. |
KF-D547Mo |
Fe5Mn5Si10Ni13Cr
Iron-base alloy powder |
-140+325目（mesh） |
HRC 35-40, (Working Temperature): ≤450℃.
Welding layer with good properties of high temperature anti- scuffing, excellent hardness, used for high temperature and pressure valve welding |
KF-D577 |
Fe13Mn2Si6Ni13Cr
Iron-base alloy powder |
-140+325目（mesh） |
HRC ≥28, (Working Temperature): ≤450℃.
Good crack resistance of the solder layer, excellent surfacing process operability, plasma welding, medium temperature and high pressure valve surfacing, surfacing process is simple, easy to operate. |
Packing: bucket, vacuum packaging: It can also be packaged according to customer requirements.